Products

Application:

1. It is used as an important tempering part that requires good toughness, high strength, and large size, such as heavy machinery and high load shaft.

2. Turbine shaft with a diameter greater than 250 mm, rotor shaft of a helicopter.

3. Turbojet engine's turbine shaft, blades, high-load transmission parts, crankshaft fasteners, gears, etc.

4. It can also be used to operate rotor shafts and blades with temperatures exceeding 400 °C.

5. It can also be used to make important parts of special performance requirements after nitriding treatment. It can be used as ultra-high strength steel after low temperature tempering or after isothermal quenching.

1. Viene utilizzato come importante parte di tempra che richiede buona tenacità, alta resistenza e grandi dimensioni, come macchinari pesanti e albero di carico elevato.

2. Albero turbina con diametro maggiore di 250 mm, albero del rotore di un elicottero.

3. Albero della turbina del motore del turbogetto, pale, parti di trasmissione ad alto carico, dispositivi di fissaggio dell'albero motore, ingranaggi, ecc.

4. Può anche essere utilizzato per azionare alberi e pale del rotore con temperature superiori a 400 ° C.

5. Può anche essere utilizzato per realizzare parti importanti dei requisiti di prestazione speciali dopo il trattamento di nitrurazione. Può essere utilizzato come acciaio ad altissima resistenza dopo la tempera a bassa temperatura o dopo tempra isotermica.

ANHUAI CO., LTD info@xingxionggroup.com for more information about the 4340 | 1.6511 | 40CrNi2MoA steel.

ANHUAI CO., LTD info@xingxionggroup.comper ulteriori informazioni sull'acciaio 4340 | 1.6511 | 40CrNi2MoA.

1.Equivalent grades/Gradi equivalenti

Germany(DIN)	USA(AISI)	UK(BS)	French(NF)	Japan(JIS)	China(GB)
1.6511	4340	816M40	40NCD3	SCM439	40CrNi2MoA

2.Chemical Composition(%)/Composizione chimica(%)

Grade	Chemical Compositon(%)
	C	Si	Mn	Cr	Mo	Ni	P	S
1.6511	0.38-0.43	0.15-0.30	0.60-0.80	0.70-0.90	0.20-0.30	1.65-2.00	≤0.035	≤0.040
4340	0.38-0.43	0.15-0.30	0.60-0.80	0.70-0.90	0.20-0.30	1.65-2.00	≤0.035	≤0.040
SCM439	0.38-0.43	0.15-0.30	0.60-0.80	0.70-0.90	0.20-0.30	1.65-2.00	≤0.035	≤0.040
40CrNi2MoA	0.38-0.43	0.15-0.30	0.60-0.80	0.70-0.90	0.20-0.30	1.65-2.00	≤0.035	≤0.040
816M40	0.38-0.43	0.15-0.30	0.60-0.80	0.70-0.90	0.20-0.30	1.65-2.00	≤0.035	≤0.040
40NCD3	0.38-0.43	0.15-0.30	0.60-0.80	0.70-0.90	0.20-0.30	1.65-2.00	≤0.035	≤0.040

3.Heat treatment/Trattamento termico:

(quenching at 850 degrees, coolant:oil ; tempering temperature 600 degrees; coolant: water, oil).

Steel annealing or high temperature tempering supply state Brinell hardness GBW is less than or equal to 269.